Загартування сплаву алюмінієвої котушки

Загартування сплаву алюмінієвої котушки

H1 pure work hardening condition suitable for obtaining the desired strength by work hardening without additional heat treatment

H2 working hardening and incomplete annealing; Застосовується до ступеня зміцнення, що перевищує вимоги до готового продукту, після неповного відпалу, so that the strength of the specified index products.

State of H3 work hardening and stabilization; It is suitable for products with stable mechanical properties after work hardening after low-temperature heat treatment or due to the action of heat in the process of processing.

State of H4 work hardening and paint treatment; It is suitable for the products with incomplete annealing caused by paint treatment after work hardening.

The tensile strength limit of HX1 is the intermediate value between 0 and HX2 state, less than 10% деформація.

HX2 tensile strength limit is the intermediate value between 0 and HX4 state, 15% деформація (також відомий як 114 hard worry state).

The tensile strength limit of HX3 is the intermediate value between HX2 and HX4 states.

HX4 tensile strength limit is the intermediate value between 0 and HX8 state, 35% деформація (also known asSemi-hard state).

The tensile strength limit of HX5 is the intermediate value between HX4 and HX6 states.

HX6 tensile strength limit is the intermediate value between HX4 and HX8 state, 55% deformation amount (також відомий як 3/4 hard state)

The tensile strength limit of HX7 is the intermediate value of HX8 hard state between HX6 and HX8 state.

HX8 hard state, 75% деформація (also known as full hard state)

Hx9   super hard state. At least 10N / mm2   H12   work hardening to 1 / 4 hard   h14   work hardening to 1 / 2 hard   H16   work hardening to 3 / 4 важко

H18   work hardened to 4 / 4 важко, тобто. fully hardened;

H19   super work hardened. The tensile strength of this material should be more than 10N / mm2 higher than that of the material in   h18 state;

H22   after work hardening, part annealing to 1 / 4 важко;

H24   after work hardening, part annealing to 1 / 2 важко;

H26   after work hardening, part annealing to 3 / 4 важко;

h28   after work hardening, part annealing to 4 / 4 важко;

H32   after work hardening, stabilizing to 1 / 4 важко;

H34   stabilization after work hardening Treatment to 1 / 2 важко;   H36   stabilizing treatment to 3 / 4 hard after work hardening;

h38   stabilizing treatment to 4 / 4 hard after work hardening;

H42   painted after work hardening, 1 / 4 важко;

h44   painted after work hardening, 1 / 2 важко;   h46 painted after work hardening, 3 / 4 важко;

h48   painted after work hardening, 4 / 4 важко;

Hxx4   use the corresponding hxx state plate, patterned plate with machining.

hxx5   to machine the state of hardened welded pipe.

h111  final annealing, then a small amount of work hardening (ratio

H11 has a light degree of hardening). This hardening is caused by operations such as stretching or straightening.

h112   hot work forming, then light work hardening, or light work hardening after a small amount of cold work, to meet the specific mechanical property requirements. A kind of

H116   a special status code set for 5xxx alloy with magnesium content no less than 4%. The aluminum-magnesium alloy material in this status has reached the set mechanical property level and good anti-stripping corrosion