1060 ALUMINUM SHEET DESCRIPTION：
1060 aluminum sheet is pretty similar to 1050 aluminum alloy with more than 0.1% of aluminum by weight. Both 1050 and 1060 aluminium sheet of Huawei AL, lives up to ISO standards, but they cover different ASTM standards. 1060 aluminium sheet contains 0.05% cooper, thus, its conductivity is 55%. Besides, 1060 aluminium sheet is relatively low strength, essentially pure aluminium alloy with many different tempers, such as O (annealed), H12, H14, H16, H18, etc. what’s more, other aluminium sheet belonging to commercial pure wrought family are available, including 1050, 1070, 1100 and so on and so forth.
Hot sale thickness: 1mm, 42mm
1060 ALUMINUM SHEET MANUFACTURING PROCESS
1060 ALUMINUM SHEET FEATURE：
1060 aluminum sheet Have good elongation and tensile strength, can satisfy completely the requirements of conventional processing (stamping, stretch) high formability. For industrial pure aluminium, high plasticity, corrosion resistance, electrical conductivity and thermal conductivity, but strength is low, heat treatment can not be improved machinability is bad; Gas welding, hydrogen welding and resistance welding, is not easy to brazing; Under various pressure processing and extension, bending.
1060 ALUMINUM SHEET CHEMICAL COMPOSITION：
1060 Aluminum sheet Machinability
The machinability of AL 1060 is fair to poor, especially in the soft temper conditions. In the harder (cold worked) tempers such as H16 and H18 the machining characteristics are improved. Either carbide or high-speed steel tooling may be used and use of lubricants is recommended, although some cutting may be done dry.
The heat treatment process of 1060 aluminum sheet
Fast annealing: the heating temperature is 350~410 degrees centigrade; with the effective thickness of the material, the heat preservation time is between 30 and 120min; cooling in air or water.
High temperature annealing: the heating temperature is 350~500 DEG C; if the finished thickness is not less than 6mm, the holding time is 10 ~ 30min, if the thickness is less than 6mm, heat until all the sheet is hot, cooling in the air.
Low temperature annealing: the heating temperature is 150~250 degrees centigrade; the heat preservation time is 2 ~ 3H; cooling in air or water.
1060 ALUMINUM SHEET APPLICATIONS:
1060 aluminum sheet is widely used in signs, billboards, building exterior decoration, bus body, tall buildings and factory wall body adornment, kitchen sink, lamp holder, fan blade, electronic parts, chemical equipment, mechanical parts, deep drawing of sheet or spinning concave ware, welding part, heat exchanger, clock surface and plate, plate, kitchenware, ornaments, reflective equipment, etc.
RELEVANT GRADE OF 1060 ALUMINUM SHEET:
|Relevant grade of 1060 Aluminum Sheet|
1060 ALUMINUM SHEET PACKING：
1060 Aluminum Sheet of packaging meet the export standard. Plastic film and brown paper can be covered at customers’ need. wooden case or wooden pallet is adopted to protect products from damage during the delivery.