Con el desarrollo de vehículos de nueva energía, la demanda de cajas de batería de gran tamaño ha aumentado significativamente. 3003 aluminium alloy strip is widely used for its ease of forming, excelentes propiedades generales de procesamiento mecánico, buena resistencia a la corrosión, fuerza moderada con gravedad específica ligera y fuerte resistencia a la explosión.
3003 tira de aluminio
Raw material for power battery case--3003 aluminium alloy strip performance requirements
Power battery shells require a high level of overall material performance:
(1) The power battery case is formed by stamping, which has a large deformation, many stamping processes, complex stamping technology, precise mould design and is an asymmetric box stamping. The performance of the material is one of the most important basic conditions for the success of the stamping process and must have good deep-drawing properties and the mechanical properties must be stable within a strict range.
(2) In order to provide effective protection for the internal battery structure, the power cell shell must have sufficient strength and hardness, while ensuring the necessary plasticity.
3003 aluminum alloy power battery shell strip
(3) In order to adapt to different environments and to ensure the service life of the battery, the material used for the power cell shell must have good corrosion resistance and chemical stability.
Main technical quality indicators for 3003 tiras de aleación de aluminio para carcasas de baterías de potencia
Las propiedades mecánicas de 3003 aluminium alloy strips for power battery shells are shown in Table 1, and the strip thickness tolerances are shown in Table 2.
| Aleación | Fuerza de Tensión (MPa) | Fuerza de producción (MPa) | Alargamiento (%) | Ear-making rate (%) |
| 3003-H14 | 135~175 | ≥135 | ≥4 | ≤4 |
Mesa 1: mechanical properties of 3003 aluminum alloy power battery case
| espesor (mm) | Tolerancia de grosor (mm) |
| >0.80~1.50 | ±0.015 |
| >1.50~3.00 | ±0.02 |
Mesa 2: 3003 Aluminum Alloy Power Battery Shell Strip Thickness Tolerance
The surface roughness of the 3003 tira de aluminio is controlled at 0.20~0.35μm, and the surface is required to be bright and clean, without defects such as periodic sticky wounds and marks, no obvious bright or dark bands, sin corrosión, penetrating porosity, pressure scratches, indentaciones metálicas y no metálicas.