Móc 1 mm arkusz aluminium be bent?
Pierwszy, najważniejszy jest temperament. The temper of the arkusz aluminium is divided into full hard, półtwardy, i łagodnych temperamentach (zwykle miękki temperament nazywany jest temperamentem O).
Efekt twardego gięcia jest w zasadzie niemożliwy (the temper of the arkusz aluminium is H18, H19, H38, itp. wszystkie są trudne)
The semi-rigid arkusz aluminium can basically be bent (H24 is also semi-rigid)
O-temper bending is definitely no problem, ale dlatego, że jest za miękki, it is basically less used in this temper.
The second is whether you choose pure aluminum or alloy aluminum
The hardness of pure aluminum is not very good. It can be used with 1100, 1050, 1060, itp., 1100 H24 is recommended.
The alloy aluminum has a better hardness, and it can be used in semi-hard tempers such as 3003, 3005, I 5052.
It is recommended that the sample be re-determined for specific conditions. If the hardness of 6061, 2024, 7075 is too high, especially in the T6 temper, it should not be bent unless it is heated and then folded.